VpCI-368D Solvent Based Temporary Coating

VpCI-368D Solvent Based Temporary Coating

PRODUCT DESCRIPTION:

VpCI®-368D is a fast drying, solvent- based temporary coating that provides protection in harsh, outdoor, unsheltered applications yet is easily removed with alkaline cleaners such as VpCI®-414. Provides multi-metal protection. Can be matched to some custom colors.

Service Hotline:+86-0532-80989502,+86-135-0535-2885
E-Mail:zzgvci@163.com

Commercial equivalent to MIL– PRF – 16173E (Grades 1 & 2), NATO  6850-66-132-5848, 6099,NSN 8030-00-062-6950, 231-2345, 244-1300, 470-2601.

PACKAGING & STORAGE

VpCI®-368D is available in 5 gallon (19 liter) pails, 55 gallon (208 liter) metal drums, liquid totes, and bulk.

To ensure best product performance, store in original packaging, indoors, and out of direct sunlight at 40-100 °F (4-38 °C).
Shelf life: 2 years


CHARACTERISTICS/TECHNICAL DATA

Volume Solids

39.22%

Gloss (ASTM D532)

NA

VOCs (ASTM D3960)

3.8 lbs/gal (464 g/L)

Viscosity

50-60 sec+ Zahn#2

Pencil Hardness (ASTM D3363)

NA

Spreading Rate

629 sq.ft./gal @ 1.0 mils DFT

(15.4 sq.m/L @ 25 μm)

Weight per Gallon

7.51 lbs/gal (.90 kg/L)

Flash Point

133 °F (56 °C)

Recommended DFT

2.0-3.0 mils (50-75 μm)

Recommended WFT

5.1-7.6 mils (130-190 μm)

Dry to Touch

30 min

Dry to Handle

60 min

Recoat Time

NA

Force Dry

15-20 min @ 150 °F (65 °C)

Full Cure

3-7 days

Salt Spray (ASTM B117)

1500 hrs

Humidity (ASTM D1748)

2500 hrs

Adhesion (ASTM D3359)

NA

Flexibility (ASTM D522)

½" mandrel (1.27 cm)

All tests performed after a 7 day cure at ambient temperature



APPLICATION

Surface Preparation

Substrate should be free of grease, oil, dirt, fingerprints, drawing compounds, rust inhibitors (except Cortec® ap- proved), or any other surface contamination that could affect adhesion. Cortec® recommends a mini,um of a SSPC-SP1 over painted surfaces. For bare metal applica- tions, Cortec® recommends a NACE #3/ SSPC-SP6. Consult Cortec® Technical Service and/or test system adhesion prior to full scale application.

Power agitate to a uniform consistency using a “squirrel cage” type mixer, hand-held drill mixer, or other equivalent method. VpCI®-368D can be applied by spray, roll, brush, or dip.

Typical Equipment Setups

HVLP / Conventional Spray
•Tip 0.02”-0.11” (0.5-2.8 mm)* dependent upon pressures and viscosity
•Air Pressure 45-55 psi
•Fluid Pressure 10 psi
•Fluid hose should be ⅜” (0.95 cm) I.D. with a maximum length of 50 feet (15.2 m). ¼” (0.64 cm) I.D. fluid hose can be used but pressures may need to be adjusted. Pot should always have dual regulation and be kept at same elevation as spray gun.

Air Assisted Airless / Airless
•Tip 0.015”-0.035” (0.38-0.89 mm)* dependent upon pres- sures and viscosity
•Pressure 1800-2500 psi
•Hose should be ⅜” (0.95 cm) I.D. minimum, but a ¼” (0.64 cm) I.D. whip end section may be used for ease of applica- tion. A maximum length of 100 feet (30.5 m) is suggested.

*All tests performed after a 7 day cure at ambient temperature

Cleanup

Clean tools/equipment immediately after use with butyl acetate when coating is still wet. When dry, use butyl cellu- solve or MEK. Follow mfg’s safety recommendations when using any solvent.


Qingdao Cortec Rust Proof Materials Co., Ltd.,               

Wechat QR code on the left side of the website

Qingdao Cortec Rust Proof Materials Co., Ltd.,

Consultation hotline:0532-80989502

Sales Hotline:135-0535-2885

E-mail:zzgvci@163.com

QQ:592192408

Address:Room 2073, No. 12, chongmingdao
East Road, Qingdao Economic Development Zone

Alibaba store:https://shop1420649126784.1688.com

Copyright:Qingdao Cortec Rust Proof Materials Co., Ltd.